Sulphur
– IMDG Code (IMO International Maritime Dangerous Goods Code) Class 4.1:
Is a relatively cheap commodity, which is used in the manufacture of fertilizer. It is not only a byproduct of the petrochemical industry, but also found in its natural form. After processing, it is often shipped in prilled form. Substantial quantities of sulphur are produced in the Alberta province of Canada, most of which is shipped from Vancouver. It is shipped from other ports, including San Francisco, Long Beach, Aqaba and Jubail.
Dry sulphur does not react with bare steel, but wet sulphur (sulphur containing free water) is potentially highly corrosive. Cargoes of sulphur in bulk are normally afforded exposed storage and are thus subject to inclement weather and consequent moisture content. The stock will also include a percentage of sulphur dust particles. In order to prevent contaminated air emissions, it is the practice, especially in Canada and the USA, where loading wharves are situated in built-up areas and the dust is considered to be a pollutant, for the environmental authorities to insist upon the use of a water spray during handling to keep down the dust. This practice, now widely adopted in other loading ports, may lead to difficulties during and after the period of ocean transportation. Despite the fact that very large quantities of sulphur are carried annually by sea, the vast majority are carried without significant damage to the carrying vessels.
Corrosion When sulphur is loaded, any retained free water filters to the bottom of the holds during the voyage. From there it is pumped out via the bilges. Some water remains on the tank tops, and together with the fines, produces a sulphurous mud. A great deal of research has been undertaken to understand and mitigate corrosion to vessels’ structures during the handling and transportation of sulphur. There are two processes whereby a corrosion reaction can occur, namely acidic and electrochemical corrosion.
Acidic corrosion: This involves a reaction between an acid and elemental iron (steel). The acid involved is sulphuric acid (H2SO4). Corrosion does not become significant until the acidity of the solution increases to or below pH2.
Electrochemical corrosion: It has been established that the electrochemical reaction involves a redox (reduction/oxidation) reaction between iron and sulphur. The specific requirements for this reaction to take place are that sulphur and iron are in direct contact and that the sulphur must be wet.
Experience has shown that it is electrochemical rather than acidic corrosion that is responsible for the largest proportion of damage occurring to a ship’s hold structures on passage.
The IMO Code of Practice for Solid Bulk Cargoes (IMSBC Code) states, in Section 9.3.1.10: “Materials which present corrosive hazards of such intensity as to affect either human tissue or the ship’s structure should only be loaded after adequate precautions and protecting measures have been taken.”
The following prudent measures, to preclude risk of damage as a result of loading sulphur, should be adopted:
Make good all damages to paint coatings on hopper tank plating, bulkheads, bulkhead stools, internal ship’s side plating frames and internals to the height to which the cargo will be in intimate contact, and loose rust and scale removed from the underside of hatchcovers. Aluminium or epoxy resin based paints appear to be most effective. Whereas the current rules of Classification Societies do not require tank top plating to be coated, it is important and accepted that paint coatings serve to provide protection to the plates during the carriage of sulphur.
Lime wash as per owner’s/shipper’s/charterer’s instructions and to the satisfaction of the pre-load surveyor. Cover the bilge strainer plates with hessian.
During the loaded voyage, maintain bilge levels below tank top level. Keep a careful bilge pumping record, which should also include estimates of the volumes of water ejected from the holds. Remove all residues of sulphur from the holds upon completion of discharge and thoroughly wash down the holds with sea water and finally fresh water. Should corrosion have occurred, it must be removed by chipping or shot blasting before washing. The bare steel touched up with paint coatings.
The presence of chlorides – in the form of salts, such as sodium and potassium chlorides – can hasten the interaction between the moist sulphur and ship’s steel. Sodium chloride is for example, a major constituent of both salt cake and dissolved materials found in sea water, while potassium chloride (potash) is regularly shipped from Vancouver. Any trace of these substances will lead to an accelerated corrosion effect, so hold cleanliness prior to loading is of the utmost importance.
To summarise, in order to determine if a vessel is likely to suffer from corrosion damage due to the carriage of wet sulphur and to what degree, the following factors should be taken into account: Cargo-related factors and in particular, residual cargo acidity. Length and duration of voyage. Temperatures encountered during the voyage. Effectiveness of lime washing and condition of underlying paint coating Proper bilge pumping to remove excess water.
Cleanliness Prior to loading sulphur, it is recommended that the receiving holds should be in a ‘grain clean’ condition, which requires: Removal of all residues of previous cargoes, hard and loose scale from the holds. Access to the upper regions of the holds should be gained by safe equipment. Air wands should be used to dislodge residues of cargo from otherwise inaccessible areas. Thoroughly wash out the holds with sea water, then Thoroughly wash out the holds with fresh water.
The IMO IMSBC code also states : “After discharge of materials, a close inspection should be made for any residue, which should be removed before the ship is presented for other cargo; such an inspection is particularly important when materials having corrosive properties have been transported.”
Gas emissions Hydrogen sulphide:
There are circumstances during the passage and after discharge whereby bulk sulphur can emit small quantities of hydrogen sulphide gas. All areas in which sulphur is stowed or used or which require the presence of personnel should therefore be thoroughly ventilated.
Sulphur dioxide:
Masters should also be aware of the possibility that sulphur dioxide may be generated during repairs involving heating/ welding in spaces previously exposed to sulphur. Appropriate safety measures should be taken.
Flammability:
Masters should be aware that fire might occur when dry sulphur is being loaded as a result of static electricity building up on the loading pipes. These fires can be extinguished by dowsing with sulphur or by the use of a fresh water spray.
Ferrous sulphide is pyrophoric (may spontaneously combust on contact with air) and can cause fires near the tank tops during discharge. Such fires maybe be controlled with the judicious use of a fine jet of fresh water.
——–